Bio-aromatics (benzene, toluene, xylenes, BTX) were prepared by the catalytic pyrolysis of six different black liquors using both in situ and ex situ approaches. A wide range of catalysts was screened and conditions were optimized in microscale reactors. Up to 7 wt % of BTX, based on the organic fraction of the black liquors, was obtained for both the in situ and ex situ pyrolysis ( T = 500-600 °C) using a Ga-modified H-ZSM-5 catalyst. The in situ catalytic pyrolysis of black liquors from hardwood paper mills afforded slightly higher yields of aromatics/BTX than softwood black liquors, a trend that could be confirmed by the results obtained in the ex situ catalytic pyrolysis. An almost full deoxygenation of the lignin and carbohydrate fraction was achieved and both organic fractions were converted to a broad range of (substituted) aromatics. The zeolite catalyst used was remarkably stable and even after 100 experiments in batch mode with intermittent oxidative catalyst regeneration, the yields and selectivity toward BTX remained similar. The ex situ pyrolysis of black liquor has potential for large-scale implementation in a paper mill without disturbing the paper production process.
MULTIFILE
The catalytic conversion of oleic acid to aromatics (benzene, toluene, and xylenes, BTX) over a granular H-ZSM-5/Al2O3 catalyst (ϕ 1.2–1.8 mm, 10 g loading) was investigated in a continuous bench-scale fixed-bed reactor (10 g oleic acid h–1). A peak carbon yield of aromatics of 27.4% was obtained at a catalyst bed temperature of 550 °C and atmospheric pressure. BTX was the major aromatics formed (peak carbon yield was 22.7%), and a total BTX production of 1000 mg g–1 catalyst was achieved within a catalyst lifetime of 6.5 h for the fresh catalyst. The catalyst was deactivated due to severe coke deposition (ca. 22.1 wt % on the catalyst). The used catalyst was reactivated by an ex situ oxidative regeneration at 680 °C in air for 12 h. The regenerated catalyst was subsequently recycled, and in total, 7 cycles of reaction-regeneration were performed. A gradual decrease in the peak carbon yield of BTX was observed with reaction-regeneration cycles (e.g., to 16.3% for the catalyst regenerated for 6 times). However, the catalyst lifetime was remarkably prolonged (e.g., >24 h), leading to a significantly enhanced total BTX production (e.g., 3000 mg g–1 catalyst in 24 h). The fresh, used, and regenerated catalysts were characterized by N2 and Ar physisorption, XRD, HR-TEM-EDX, 27Al, and 29Si MAS ssNMR, NH3-TPD, TGA, and CHN elemental analysis. Negligible changes in textural properties, crystalline structure, and framework occurred after one reaction-regeneration cycle, except for a slight decrease in acidity. However, dealumination of the H-ZSM-5 framework was observed after 7 cycles of reaction-regeneration, leading to a decrease in microporosity, crystallinity, and acidity. Apparently, these changes are not detrimental for catalyst activity, and actually, the lifetime of the catalyst increases, rationalized by considering that coke formation rates are retarded when the acidity is reduced.
Sustainable production of aromatics, especially benzene, toluene and xylenes (BTX), is essential considering their broad applications and the current global transition away from crude oil utilization. Aromatization of lower olefins, particularly ethene and propene, offers great potential if they are derived from more circular alternative carbon feedstocks such as biomass and waste plastics. This work aims to identify the preferred olefin feed, ethene or propene, for BTX production in a fixed-bed reactor. A commercial H-ZSM-5 (Si/Al = 23) catalyst was used as a reference catalyst, as well as a Ga-ZSM-5 catalyst, prepared by Ga ion-exchange of the H-ZSM-5 catalyst. At 773 K, 1 bar, 45 vol % olefin, 6.75 h−1, propene aromatization over the Ga-ZSM-5 catalyst exhibited higher BTX selectivity of 55 % and resulted in slower catalyst deactivation compared to ethene aromatization.
Paper sludge contains papermaking mineral additives and fibers, which could be reused or recycled, thus enhancing the circularity. One of the promising technologies is the fast pyrolysis of paper sludge, which is capable of recovering > 99 wt.% of the fine minerals in the paper sludge and also affording a bio-liquid. The fine minerals (e.g., ‘circular’ CaCO3) can be reused as filler in consumer products thereby reducing the required primary resources. However, the bio-liquid has a lower quality compared to fossil fuels, and only a limited application, e.g., for heat generation, has been applied. This could be significantly improved by catalytic upgrading of the fast pyrolysis vapor, known as an ex-situ catalytic pyrolysis approach. We have recently found that a high-quality bio-oil (mainly ‘bio-based’ paraffins and low-molecular-weight aromatics, carbon yield of 21%, and HHV of 41.1 MJ kg-1) was produced (Chem. Eng. J., 420 (2021), 129714). Nevertheless, catalyst deactivation occurred after a few hours’ of reaction. As such, catalyst stability and regenerability are of research interest and also of high relevance for industrial implementation. This project aims to study the potential of the add-on catalytic upgrading step to the industrial fast pyrolysis of paper sludge process. One important performance metric for sustainable catalysis in the industry is the level of catalyst consumption (kgcat tprod-1) for catalytic pyrolysis of paper sludge. Another important research topic is to establish the correlation between yield and selectivity of the bio-chemicals and the catalyst characteristics. For this, different types of catalysts (e.g., FCC-type E-Cat) will be tested and several reaction-regeneration cycles will be performed. These studies will determine under which conditions catalytic fast pyrolysis of paper sludge is technically and economically viable.